Kimya ABS Kevlar Filament – Black (2.85mm, 0.5kg)
$58.20
Product Description
ABS Kevlar is a composite filament enriched in aramid fibers. It offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion.
Kimya ABS Kevlar properties:
- Low warpage - compared to ABS-S
- Lighter-weight printed parts - compared to ABS Carbon
- Complies with the REACH standard
Specifications
| Model | PS2001TQ |
|---|---|
| Manufacturer |
FILAMENT PROPERTIES
| Properties | Test Methods | Values |
| Diameter | INS-6712 |
1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.036 g/cm3 |
| Moisture rate | INS-6711 | < 0.5% |
| Melt flow index (MFI) (@225°C – 2.16 kg) | ISO 1133-1 | 35 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 | 100 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| Printing Direction | XY |
| Printing Speed | 40-70 mm/s |
| Infill | 100% – rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 250-270°C |
| Bed T° | 90-100°C |
PRINTED SPECIMENS PROPERTIES
| Mechanical Properties | Test Methods | Values |
| Tensile Modulus | ISO 527-2/5A/50 | 2,188 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 30.4 MPa |
| Elongation at Tensile Strength | ISO 527-2/5A/50 | 1.8% |
| Tensile Stress at Break | ISO 527-2/5A/50 | 27.3 MPa |
| Tensile Elongation at Break | ISO 527-2/5A/50 | 3.5% |
| Flexural Modulus | ISO 178 | 1,662 MPa |
| Deformation at flexural strain | ISO 178 | > 4.4% |
| Charpy impact resistance | ISO 179-1/1eA | 5.1 kJ/m² |
| Shore Hardness | ISO 868 | 70,1D |
Related Products
Sale!
Kimya White PLA-HI Filament (2.85mm, 0.75kg)
$27.74
Formulated to quadruple its impact resistance compared to PLA-S
Add to cart More Information
Kimya Black PLA-R Filament (2.85mm, 0.75kg)
$28.00
PLA-R Black is biodegradable eligible
Add to cart More Information
Kimya White TPU-92A Filament (2.85mm, 0.75kg)
$43.50
For printing flexible and solvent resistant parts
Add to cart More Information
Kimya PEBA-S Filament – Translucent (2.85mm, 0.5kg)
$58.80
PA2001TQ
Optimized for tensile elongation applications