Kimya Black PLA-HI Filament (2.85mm, 0.75kg)

Original price was: $34.68.Current price is: $27.74.

Buying a PLA-HI filament reel means choosing a classic filament revisited for optimized and responsible 3D printing:

PLA filament (Poly-Lactic Acid) is a light and durable technical thermoplastic, which offers a quality alternative to other plastics traditionally used for 3D printing, standard PLA and ABS. It combines the ease of printing PLA filament with the mechanical characteristics of ABS filament.

A 100% versatile filament to materialize all your ideas in 3D

Ease of printing & mechanical strength. PLA-HI is an easy-to-print filament. Its regularity prevents blockage of the nozzle during printing. Its printing does not require a heating plate. Visual quality: excellent quality of room and surface finish. Postproduction is easy, but not necessary, given the quality of rendering.

PLA-HI is more impact resistant than ABS while retaining the ease of printing a PLA. Our formulation modifications give the PLA-HI a tensile modulus and a percentage of elongation comparable to those of ABS while maintaining its ease of printing. The environmental responsibility and more. The PLA-HI is the ideal filament to create parts like functional prototypes or spare parts, for model making, architectural models ...

A bio-sourced PLA-HI filament

Kimya 3D coils and filaments are made from upgraded plastics, such as used ink cartridges, collected and recycled by ARMOR. In combination with a collection service, Kimya PLA-HI 3D coils and filaments are designed to be fully recycled after use. The filament coils are made from 100% upgraded used ink cartridges. PLA-HI is derived from natural materials such as corn starch or cane sugar.

Ask our Experts

Call Us | Email Us | Request Callback


Model PL2090TQ


Properties Test Methods Values
Diameter INS-6712

1.75 ± 0.1 mm

2.85 ± 0.1 mm

Density ISO 1183 1.21 g/cm3
Moisture rate INS-6711 10
Melt flow index (MFI) (@210°C – 2.16 kg) ISO 1133 5.7 g/10min
Glass transition temperature (Tg) ISO 11357 60 °C
Melting Temperature (Tm) ISO 11357 DSC (10°C/min – 20-220°C) 156 °C



Printing Direction XY
Printing Speed 50 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 200°C
Bed T° 60°C


Mechanical Properties Test Methods Values
Tensile Modulus ISO 527 2,491 MPa
Tensile Strength ISO 527 43 MPa
Elongation at Tensile Strength ISO 527 2%
Tensile Stress at Break ISO 527 22.9 MPa
Tensile Elongation at Break ISO 527 4.2%
Flexural Modulus ISO 178 2,097 MPa
Flexural stress at conventional deflection (3,5% strain) ISO 178 62.8 MPa
Charpy impact resistance (Charpy – notched type A) ISO 179 16.5 kJ/m²
Store Hardness ISO 868 76,8D